Los kho cov huab cua tsis kam ntawm covROJ KUB-EURER ZEAM (HORK)Nyob rau hauv welded huab cua hlau (piv txwv li, Q460NH, Corten), ua raws cov kauj ruam kev ua haujlwm:
1. Post-Weld Sib Tsoo
Lub hom phiaj: Tshem tawm cov Haz hlau Metallurgically hloov txheej.
Txojkev:
Gr zom weams thiab haz rau ib tug tob ntawm0.5-1 hli(kom txog thaum muaj kev sib xws hlau pib hlau tshwm).
Kev siv120-grit abrasive discskom ua tiav ib qho kev sib tw saum npoo (RA) ntawmTsawg dua los yog sib npaug rau 3.2 μm.
Ua rau: Tshem tawm microstration microstructural heterogeneity uas cuam tshuam patina tsim.
2. Tshuaj Patina nrawm nrawm
Lus teb: Thov5% tooj liab sulfate (cuso₄) + 1}}}} phosphoric acid (h ₃po₄)rau lub haz.
Kev ua:
Ntxuav cov nplaim nrog acetone.
Txau qhov kev daws qhov tsis meej.
Yaug tom qab30 feebthiab nthuav tawm rau huab cua.
Qho kawg: Tawm tsam oxidation sai sai, tsim kev tiv thaivFeooh / cu-nplua nuj txheejnyob hauv48 teev.
3. Zos txheej
Rau cov chaw hnyav(Nqaum / Muaj):
Ua ntaub ntawvZinc-nplua nuj Primer(piv txwv li, zrc txias galvanizing compound) rau lub haz.
Qhov tuab:50–80 μm.
Kev ceeb toom: Zinc txi cov hlau kom txog thaum lub sijhawm Patina ib txwm hloov dua siab (6-12 lub hlis).
4. Thermal stabilization
Kev ua: Post-weldNrov Kev Kho Cua Sovntawm250-300 degreerau1 teev.
Lub tshuab:
Txo cov kev ntxhov siab ntau dua.
Txhawb nqa CU / Criffusion los txhim kho kev ua kom haum taub hau corrosion.
5. Txheeb xyuas kev soj ntsuam
Kev Ntsuas Cov Ntsev(ASTM B117):
Txais Tus Nqi Kub Huam Corrosion:Tsawg dua los yog sib npaug rau 0.1 mm / xyoo(thiab cov hlau hluav taws xob hauv 0.05 mm / xyoo).
Daim nplaum(ISO 4624):
Patina txheej yuav tsum tau tiv thaivNtau dua los yog sib npaug rau 3 MParub tawm kev ntxhov siab.