GL Ship Class Steel Phaj / Nkoj steel phaj / dej hiav txwv platform
GL Ship Class Steel Phaj Qib:
GL A420 GL D420 GL E420 GL F420
GL A460 GL D460 GL E460 GL F460
GL A500 GL D500 GL E500 GL F500
GL A550 GL D550 GL E550 GL F550
GL A620 GL D620 GL E620 GL F620
GL A690 GL D690 GL E690 GL F690
GL Ship Class Steel Phaj Ntau Lawm:
Thickness: 4 hli - 200 hli;
Dav: 1000mm- 4000mm;
Ntev: 4000mm- 12000mm.
Muaj peev xwm tsim tau:
100000 Tons Ib Hlis.
Txoj kev tsim khoom:
Kub Rolled
Technical Requirements & Additional Services rau GL GL Ship Class steel phaj:
♦ Kev ntsuam xyuas siab
♦ Z-Test (Z15, Z25, Z35)
♦ Qhov ntsuas kub tsis tshua muaj kev cuam tshuam
♦ Kev txhaj tshuaj blasting thiab pleev xim, txiav thiab vuam raws li tus neeg siv khoom kawg
GL Qib A420 Shipbuilding Steel Phaj Chemical Composition thiab Mechanical Property
| C max | Si max | Mn | P max | S max | N max. |
|
0.21 |
0.55 | 1.70 |
0.030 |
0.030 |
0.020 |
| Yield zog (MPa) min. | Tensile zog (MPa) | Elongation min. % |
| 420 | 530-680 | 18 |
GL Qib D420 Shipbuilding Steel Phaj Chemical Composition thiab Mechanical Property
| C max | Si max | Mn | P max | S max | N max. |
|
0.20 |
0.55 | 1.70 |
0.025 |
0.025 |
0.020 |
| Yield zog (MPa) min. | Tensile zog (MPa) | Elongation min. % |
| 420 | 530-680 | 18 |
GL Qib E420 Shipbuilding Steel Phaj Chemical Composition thiab Mechanical Property
| C max | Si max | Mn | P max | S max | N max. |
|
0.20 |
0.55 | 1.70 |
0.025 |
0.025 |
0.020 |
| Yield zog (MPa) min. | Tensile zog (MPa) | Elongation min. % |
| 420 | 530-680 | 18 |
GL Qib F420 Shipbuilding Steel Phaj Chemical Composition thiab Mechanical Property
| C max | Si max | Mn | P max | S max | N max. |
|
0.18 |
0.55 | 1.60 |
0.020 |
0.020 |
0.020 |
| Yield zog (MPa) min. | Tensile zog (MPa) | Elongation min. % |
| 420 | 530-680 | 18 |
GL Qib A460 Shipbuilding Steel Phaj Chemical Composition thiab Mechanical Property
| C max | Si max | Mn | P max | S max | N max. |
|
0.21 |
0.55 | 1.70 |
0.030 |
0.030 |
0.020 |
| Yield zog (MPa) min. | Tensile zog (MPa) | Elongation min. % |
| 460 | 570-720 | 17 |
GL GRade D460 Shipbuilding Steel Phaj Chemical Composition thiab Mechanical Property
| C max | Si max | Mn | P max | S max | N max. |
|
0.20 |
0.55 | 1.70 |
0.025 |
0.025 |
0.020 |
| Yield zog (MPa) min. | Tensile zog (MPa) | Elongation min. % |
| 460 | 570-720 | 17 |
GL Qib E460 Shipbuilding Steel Phaj Chemical Composition thiab Mechanical Property
| C max | Si max | Mn | P max | S max | N max. |
|
0.20 |
0.55 | 1.70 |
0.025 |
0.025 |
0.020 |
| Yield zog (MPa) min. | Tensile zog (MPa) | Elongation min. % |
| 460 | 570-720 | 17 |
GL Qib F460 Shipbuilding Steel Phaj Chemical Composition thiab Mechanical Property
| C max | Si max | Mn | P max | S max | N max. |
|
0.18 |
0.55 | 1.60 |
0.020 |
0.020 |
0.020 |
| Yield zog (MPa) min. | Tensile zog (MPa) | Elongation min. % |
| 460 | 570-720 | 17 |
GL Qib A500 Shipbuilding Steel Phaj Chemical Composition thiab Mechanical Property
| C max | Si max | Mn | P max | S max | N max. |
|
0.21 |
0.55 | 1.70 |
0.030 |
0.030 |
0.020 |
| Yield zog (MPa) min. | Tensile zog (MPa) | Elongation min. % |
| 500 | 610-770 | 16 |
GL Qib D500 Shipbuilding Steel Phaj Chemical Composition thiab Mechanical Property
| C max | Si max | Mn | P max | S max | N max. |
|
0.20 |
0.55 | 1.70 |
0.025 |
0.025 |
0.020 |
| Yield zog (MPa) min. | Tensile zog (MPa) | Elongation min. % |
| 500 | 610-770 | 16 |
GLQib E500 Shipbuilding Steel Phaj Chemical Composition thiab Mechanical Property
| C max | Si max | Mn | P max | S max | N max. |
|
0.20 |
0.55 | 1.70 |
0.025 |
0.025 |
0.020 |
| Yield zog (MPa) min. | Tensile zog (MPa) | Elongation min. % |
| 500 | 610-770 | 16 |
GL Qib F500 Shipbuilding Steel Phaj Chemical Composition thiab Mechanical Property
| C max | Si max | Mn | P max | S max | N max. |
|
0.18 |
0.55 | 1.60 |
0.020 |
0.020 |
0.020 |
| Yield zog (MPa) min. | Tensile zog (MPa) | Elongation min. % |
| 500 | 610-770 | 16 |
GL Qib A550 Shipbuilding Steel Phaj Chemical Composition thiab Mechanical Property
| C max | Si max | Mn | P max | S max | N max. |
|
0.21 |
0.55 | 1.70 |
0.030 |
0.030 |
0.020 |
| Yield zog (MPa) min. | Tensile zog (MPa) | Elongation min. % |
| 550 | 670-830 | 16 |
GL Qib D550 Shipbuilding Steel Phaj Chemical Composition thiab Mechanical Property
| C max | Si max | Mn | P max | S max | N max. |
|
0.20 |
0.55 | 1.70 |
0.025 |
0.025 |
0.020 |
| Yield zog (MPa) min. | Tensile zog (MPa) | Elongation min. % |
| 550 | 670-830 | 16 |
GL Qib E550 Shipbuilding Steel Phaj Chemical Composition thiab Mechanical Property
| C max | Si max | Mn | P max | S max | N max. |
|
0.20 |
0.55 | 1.70 |
0.025 |
0.025 |
0.020 |
| Yield zog (MPa) min. | Tensile zog (MPa) | Elongation min. % |
| 550 | 670-830 | 16 |
GLQib F550 Shipbuilding Steel Phaj Chemical Composition thiab Mechanical Property
| C max | Si max | Mn | P max | S max | N max. |
|
0.18 |
0.55 | 1.60 |
0.020 |
0.020 |
0.020 |
| Yield zog (MPa) min. | Tensile zog (MPa) | Elongation min. % |
| 550 | 670-830 | 16 |
GL Qib A620 Shipbuilding Steel Phaj Chemical Composition thiab Mechanical Property
| C max | Si max | Mn | P max | S max | N max. |
|
0.21 |
0.55 | 1.70 |
0.030 |
0.030 |
0.020 |
| Yield zog (MPa) min. | Tensile zog (MPa) | Elongation min. % |
| 620 | 720-890 | 15 |
GL Qib D620 Shipbuilding Steel Phaj Chemical Composition thiab Mechanical Property
| C max | Si max | Mn | P max | S max | N max. |
|
0.20 |
0.55 | 1.70 |
0.025 |
0.025 |
0.020 |
| Yield zog (MPa) min. | Tensile zog (MPa) | Elongation min. % |
| 620 | 720-890 | 15 |
GL Qib E620 Shipbuilding Steel Phaj Chemical Composition thiab Mechanical Property
| C max | Si max | Mn | P max | S max | N max. |
|
0.20 |
0.55 | 1.70 |
0.025 |
0.025 |
0.020 |
| Yield zog (MPa) min. | Tensile zog (MPa) | Elongation min. % |
| 620 | 720-890 | 15 |
GL Qib F620 Shipbuilding Steel Phaj Chemical Composition thiab Mechanical Property
|
Qib |
Chemical Composition (%) |
||||
|
C |
Mn Ntau dua lossis sib npaug |
Si |
P |
S |
|
|
wb 620 |
0.18 |
0.90-1.60 |
0.10-0.50 |
0.035 |
0.035 |
|
Qib |
Mechanical Property |
|
|||
|
Tensile zog (MPa) |
Yield zog (MPa) |
% Elongation hauv 2 nti (50mm) min |
Impacting Test Temperature (degree) |
|
|
|
wb 620 |
400-590 |
315 |
22 |
-20 |
|
GL Qib A690 Shipbuilding Steel Phaj Chemical Composition thiab Mechanical Property
| C max | Si max | Mn | P max | S max | N max. |
|
0.21 |
0.55 | 1.70 |
0.030 |
0.030 |
0.020 |
| Yield zog (MPa) min. | Tensile zog (MPa) | Elongation min. % |
| 690 | 770-940 | 14 |
GL Qib D690 Shipbuilding Steel Phaj Chemical Composition thiab Mechanical Property
| C max | Si max | Mn | P max | S max | N max. |
|
0.20 |
0.55 | 1.70 |
0.025 |
0.025 |
0.020 |
| Yield zog (MPa) min. | Tensile zog (MPa) | Elongation min. % |
| 690 | 770-940 | 14 |
GL Qib E690 Shipbuilding Steel Phaj Chemical Composition thiab Mechanical Property
| C max | Si max | Mn | P max | S max | N max. |
|
0.20 |
0.55 | 1.70 |
0.025 |
0.025 |
0.020 |
| Yield zog (MPa) min. | Tensile zog (MPa) | Elongation min. % |
| 690 | 770-940 | 14 |
GL Qib F690 Shipbuilding Steel Phaj Chemical Composition thiab Mechanical Property
| C max | Si max | Mn | P max | S max | N max. |
|
0.18 |
0.55 | 1.60 |
0.020 |
0.020 |
0.020 |
| Yield zog (MPa) min. | Tensile zog (MPa) | Elongation min. % |
| 690 | 770-940 | 14 |
GNEE Cov neeg tuaj saib
GNEE TEAM
GNEE Cov Neeg Siv Khoom Mus Saib Xyuas
GNEE Exhibition
GNEE Pab Pawg Muag Khoom
Cim npe nrov: gl nkoj chav kawm steel phaj, Tuam Tshoj gl nkoj chav kawm steel phaj manufacturers, lwm tus neeg, Hoobkas